C10 hardening steel
Unalloyed steel suitable for general use, easily cold worked and weldable without special precautions.
Some of the main characteristics of C10 steel are hardness and strength, properties that make it ideal for the production of machine parts and structural components capable of withstanding high loads as well as resisting wear and fatigue.
This type of steel also enjoys excellent workability-it is easy to shape into a variety of shapes and sizes, making it a versatile material for many industrial applications.
Hardening steel 18NiCrMo5
Due to its high toughness and hardness, 18NiCrMo5 steel is able to withstand the mechanical and thermal stresses to which the mechanical parts with which they are manufactured are subjected, ensuring long service life and good functionality.
The use of 18NiCrMo5 steel is widespread in the manufacture of transmission shafts, gears, camshafts and other machine components that require high performance and reliability.
Areas of Application
-
Grids
-
-
-
-
-
-
Distributors
-
-
-
Pump body
-
-
-
-
-
-
-
-
-
-
-
Racing parts
-
-
-
-
-
-
-
-
-
-
Engine shields
-
-
-
-
| CORRESPONDING RULES | CHEMICAL ANALYSIS | MECHANICAL CHARACTERISTICS | ||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| UNI | AISI | C% | Mn% | Si% | Cr% | Ni% | Mo% | R N/mm² | Rs N/mm² | A% min. | Hardness | |||||||||
| C10 | 1010 | 0,07÷0,12 | 0,3÷0,7 | <1,00 | (490) (883) | (=294) | (12) | HRC 55-62 | ||||||||||||
| 18NiCrMo5 | 0,15÷0,21 | 0,6÷0,9 | <1,00 | 0,7÷1,0 | 1,2÷1,5 | 0,15÷0,25 | (1230) (1520) | (=980) | (8) | HRC 55-65 | ||||||||||
NB: Data subject to change among the various foundries